UHP 500 mm Dia 20 duim oond grafiet elektrode met tepels
Tegniese parameter
Fisiese en chemiese eienskappe vir D500mm(20”) elektrode en tepel
| Parameter | Deel | Eenheid | UHP 500mm(20”) Data |
| Nominale deursnee | Elektrode | mm (duim) | 500 |
| Maksimum deursnee | mm | 511 | |
| Min deursnee | mm | 505 | |
| Nominale lengte | mm | 1800/2400 | |
| Maksimum lengte | mm | 1900/2500 | |
| Min Lengte | mm | 1700/2300 | |
| Maksimum stroomdigtheid | KA/cm2 | 18-27 | |
| Huidige dravermoë | A | 38 000-55 000 | |
| Spesifieke weerstand | Elektrode | μΩm | 4,5-5,6 |
| Tepel | 3,4-3,8 | ||
| Buigkrag | Elektrode | Mpa | ≥12,0 |
| Tepel | ≥22,0 | ||
| Young se modulus | Elektrode | Gpa | ≤13,0 |
| Tepel | ≤18,0 | ||
| Bulkdigtheid | Elektrode | g/cm3 | 1,68-1,72 |
| Tepel | 1,78-1,84 | ||
| CTE | Elektrode | ×10-6/℃ | ≤1.2 |
| Tepel | ≤1,0 | ||
| As inhoud | Elektrode | % | ≤0,2 |
| Tepel | ≤0,2 |
LET WEL: Enige spesifieke vereiste oor dimensie kan aangebied word.
Aansoeke
- Elektriese boogoond
Grafietelektrode word hoofsaaklik in die moderne staalvervaardigingsproses gebruik, Electric Arc Furnace word wyd erken as een van die doeltreffendste en betroubaarste gereedskap. ’n Elektriese boogoond gebruik grafietelektrodes om hoë temperature te skep en stroom op te wek, wat dan gebruik word om herwonne staalskroot te smelt. Aangesien die deursnee van die grafietelektrode 'n belangrike rol speel om die nodige vlak van hitte te skep en 'n hoë-gehalte eindproduk te verseker, is die gebruik van die regte elektrode van kardinale belang om optimale resultate te behaal. Volgens die kapasiteit van die elektriese oond word grafietelektrodes met verskillende deursnee toegerus om die grafietelektrodes steeds te laat gebruik, die grafietelektrode word deur tepels verbind. - Ondergedompelde elektriese oond
Die ondergedompelde elektriese oond is 'n revolusionêre produk wat ontwerp is om aan die behoeftes van die moderne industrie te voldoen. Hierdie moderne oond beskik oor 'n UHP-grafietelektrode wat spesiaal vervaardig is om die doeltreffendheid van die smeltproses te verbeter. Die grafietelektrode in die ondergedompelde elektriese oond word hoofsaaklik gebruik om ferrolegerings, suiwer silikon, geel fosfor, mat en kalsiumkarbied te vervaardig. Die unieke ontwerp van hierdie elektriese oond onderskei dit van tradisionele oonde, aangesien dit toelaat dat 'n deel van die geleidende elektrode in die laaimateriaal begrawe word. - Weerstand oond
Weerstandoonde word gebruik om grafietprodukte van hoë gehalte soos UHP-grafietelektrodes te vervaardig. Hierdie elektrodes word wyd gebruik in die elektriese boogoond-staalvervaardigingsproses om hoëprestasie-staal te vervaardig. Die UHP-grafietelektrode is bekend vir sy hoë termiese geleidingsvermoë, lae elektriese weerstand en weerstand teen termiese skok. Hierdie eienskappe maak hulle 'n ideale keuse vir die staalvervaardigingsproses. UHP grafiet elektrodes word vervaardig deur 'n hoë-temperatuur grafitisering proses binne 'n weerstand oond.
Gufan Cabon Koniese tepel en sok tekening
Gufan Koolstof Koniese tepel en sok afmetings (4TPI)
| Gufan Koolstof Koniese tepel en sok afmetings (4TPI) | |||||||||
| Nominale deursnee | IEC-kode | Groottes van tepel (mm) | Groottes van sok (mm) | Draad | |||||
| mm | duim | D | L | d2 | I | d1 | H | mm | |
| Verdraagsaamheid (-0.5～0) | Toleransie (-1~0) | Toleransie (-5~0) | Toleransie (0–0,5) | Verdraagsaamheid (0–7) | |||||
| 200 | 8 | 122T4N | 122,24 | 177,80 | 80.00 | <7 | 115,92 | 94,90 | 6,35 |
| 250 | 10 | 152T4N | 152,40 | 190,50 | 108.00 | 146,08 | 101.30 | ||
| 300 | 12 | 177T4N | 177,80 | 215,90 | 129,20 | 171,48 | 114.00 | ||
| 350 | 14 | 203T4N | 203,20 | 254,00 | 148,20 | 196,88 | 133.00 | ||
| 400 | 16 | 222T4N | 222,25 | 304,80 | 158,80 | 215,93 | 158,40 | ||
| 400 | 16 | 222T4L | 222,25 | 355,60 | 150.00 | 215,93 | 183,80 | ||
| 450 | 18 | 241T4N | 241,30 | 304,80 | 177,90 | 234,98 | 158,40 | ||
| 450 | 18 | 241T4L | 241,30 | 355,60 | 169,42 | 234,98 | 183,80 | ||
| 500 | 20 | 269T4N | 269,88 | 355,60 | 198.00 | 263,56 | 183,80 | ||
| 500 | 20 | 269T4L | 269,88 | 457,20 | 181,08 | 263,56 | 234,60 | ||
| 550 | 22 | 298T4N | 298,45 | 355,60 | 226,58 | 292,13 | 183,80 | ||
| 550 | 22 | 298T4L | 298,45 | 457,20 | 209,65 | 292,13 | 234,60 | ||
| 600 | 24 | 317T4N | 317,50 | 355,60 | 245,63 | 311,18 | 183,80 | ||
| 600 | 24 | 317T4L | 317,50 | 457,20 | 228,70 | 311,18 | 234,60 | ||
Verwante produkte
-
Grafiet elektrodes tepels 3tpi 4tpi Connectin...
Beskrywing Die grafietelektrodenippel is 'n klein maar noodsaaklike deel van die EAF-staalvervaardigingsproses. Dit is 'n silindriese komponent wat die elektrode met die oond verbind. Tydens die staalvervaardigingsproses word die elektrode in die oond laat sak en in kontak met die gesmelte metaal geplaas. Elektriese stroom vloei deur die elektrode en genereer hitte, wat die metaal in die oond smelt. Die tepel speel 'n deurslaggewende rol in die instandhouding van...
-
Koolstofblokke geëxtrudeerde grafietblokke Edm Isos...
Tegniese Parameter Fisiese En Chemiese Indekse Vir Grafietblokitem Eenheid GSK TSK PSK Korrel mm 0.8 2.0 4.0 Digtheid g/cm3 ≥1.74 ≥1.72 ≥1.72 Weerstandsvermoë μ Ω.m ≤7.5 ≤8.5 ≤8.pa ≥36 ≥35 ≥34 As % ≤0.3 ≤0.3 ≤0.3 Elastiese Modulus Gpa ≤8 ≤7 ≤6 CTE 10-6/℃ ≤3 ≤2.5 ≤2 Mpa.4 Buigsterkte 1 Po.4 Buigsterkte 1 ≥...
-
Koolstoftoevoeging Koolstofverhoger vir staalgiet...
Gekalsineerde Petroleum Coke (CPC) Samestelling Vaste Koolstof(FC) Vlugtige Materie(VM) Swael(S) Asvog ≥96% ≤1% 0≤0.5% ≤0.5% ≤0.5% Grootte:0-1mm,1-3mm, 1 -5mm of op klante se opsie Verpakking: 1.Waterdig PP geweef sakke, 25 kg per papiersak, 50 kg per klein sakke 2.800 kg-1000 kg per sak as waterdigte jumbo-sakke Hoe om gekalsineerde petroleumcoke (CPC) seer te vervaardig...
-
Oond grafiet elektrode gereelde krag RP Gra...
Tegniese Parameter Parameter Deel Eenheid RP 550mm(22”) Data Nominale Diameter Elektrode mm(duim) 550 Maks Diameter mm 562 Min Diameter mm 556 Nominale Lengte mm 1800/2400 Maks Lengte mm 1900/2500 Min Lengte mm 3000 KA Stroom /cm2 12-15 Stroomdrakapasiteit A 28000-36000 Spesifieke Weerstand Elektrode μΩm 7.5-8.5 Tepel 5.8-6.5 Buig...
-
UHP 400mm Turkye Grafiet Elektrode Vir EAF LF ...
Tegniese Parameter Parameter Deel Eenheid UHP 400mm(16”) Data Nominale Diameter Elektrode mm(duim) 400(16) Maks Diameter mm 409 Min Diameter mm 403 Nominale Lengte mm 1600/1800 Maks Lengte mm 1700/1900 Min Max Lengte/17 Stroomdigtheid KA/cm2 16-24 Stroomdravermoë A 25000-40000 Spesifieke Weerstandselektrode μΩm 4.8-5.8 Tepel 3.4-4.0 F...
-
Hoëkrag grafiet elektrode vir EAF LF Smelti ...
Tegniese Parameter Parameter Deel Eenheid HP 350mm(14”) Data Nominale Diameter Elektrode mm(duim) 350(14) Maks Diameter mm 358 Min Diameter mm 352 Nominale Lengte mm 1600/1800 Maks Lengte mm 1700/1900 Min Lengte0/1750 Stroom Digtheid KA/cm2 17-24 Stroomdrakapasiteit A 17400-24000 Spesifieke Weerstandselektrode μΩm 5.2-6.5 Tepel 3.5-4.5 Buig...